Application of technique for growth of large crystal by tilting mirror type floating zone method

倾斜镜式浮区法大晶体生长技术的应用

• 批准号: 23360340
• 负责人: WATAUCHI Satoshi
• 金额: $ 12.31万
• 依托单位: University of Yamanashi
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23360340/
• 关键词: 結晶育成; 偏析; シンチレータ; 長尺化; 単結晶育成

Pr doped Lu3Al5O12 (Pr:LuAG) crystals were grown by the infrared convergent heating floating zone (IR-FZ) method using xenon lamps as heat sources. longer crystal of Pr:LuAG was successfully grown by this method. The optical properties of these crystal were good enough as a scintillator. They were almost same with those grown by the CZ method and the IR-FZ method using halogen lamps as heat sources. The crystalinity of the crystal grown using xenon lamps was rather better than those of these crystal. The many cracks were, however, observed in these crystal. The suppression of the crack formation was found to be very important.

采用红外会聚加热浮区法（IR-FZ），以氙灯为热源，生长了Pr掺杂Lu 3Al 5 O 12（Pr：LuAG）晶体。用此方法成功地生长出Pr：LuAG长晶体。这些晶体的光学性质足够好作为闪烁体。它们与以卤素灯为热源的CZ法和IR-FZ法生长的样品几乎相同。用氙灯生长的晶体的结晶度比这些晶体好。然而，在这些晶体中观察到许多裂纹。发现抑制裂纹形成是非常重要的。

项目成果

IR-FZ法によるPr添加Lu_3Al_5O_<12>単結晶の育成

IR-FZ法生长Pr掺杂Lu_3Al_5O_<12>单晶

• 发表时间: 2013
• 作者: 蔭山直佑 ;井上博史 ;森 勇人;綿打敏司,芦沢ひとみ,長尾雅則,田中功,黒澤俊介,横田有為,吉川彰
• 通讯作者: 綿打敏司,芦沢ひとみ,長尾雅則,田中功,黒澤俊介,横田有為,吉川彰

研究者総覧

研究员名单

IR-FZ法によるPr添加Lu3Al5O12単結晶の育成

IR-FZ 法生长 Pr 掺杂 Lu3Al5O12 单晶

• 发表时间: 2013
• 作者: 井上博史 ;蔭山直佑 ;森 勇人;綿打敏司，芦沢ひとみ，長尾雅則，田中功，黒澤俊介，横田有為，吉川彰
• 通讯作者: 綿打敏司，芦沢ひとみ，長尾雅則，田中功，黒澤俊介，横田有為，吉川彰