Development of a Mold for Flash Generation Measurement

闪光产生测量模具的开发

• 批准号: 23560133
• 负责人: MURATA Yasuhiko
• 金额: $ 2.58万
• 依托单位: Nippon Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2013
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23560133/
• 关键词: プラスチック; 射出成形; 金型; 計測; バリ; 成形不良

Flash is a defect that occurs in injection molding. In this study, the flash generation measurement mold was proposed to evaluate the secondary flash generation mechanism. This mold can open the gap of arbitrary size between the mold parting faces at certain times during injection molding. Using this mold, flash generation behavior was investigated at various gap sizes between the mold parting faces and melt pressure. As a result, it was clarified that the secondary flash began to be generated immediately after the gap reached a constant size and that the secondary flash length decreased as the timing was delayed for gap opening.

飞边是注塑成型中出现的一种缺陷。在本研究中，我们提出了一个闪光产生的测量模型来评估二次闪光的产生机制。该模具可在注射成型过程中的特定时间打开模具分型面之间任意大小的差距。使用该模具，在不同的模具分型面和熔体压力之间的间隙大小的飞边产生行为进行了研究。其结果是，明确了在差距达到恒定尺寸之后立即开始产生二次闪光，并且二次闪光长度随着间隙打开的定时延迟而减小。

项目成果

射出成形におけるバリ発生評価金型の開発

开发用于评估注塑成型中毛刺发生情况的模具

• 发表时间: 2014
• 期刊: プラスチック成形加工学会誌成形加工
• 作者: 村田泰彦;菱田智大;所寛;吉田高平
• 通讯作者: 吉田高平

射出成形におけるバリ発生評価金型

用于评估注塑过程中毛刺发生情况的模具

• 发表时间: 2012
• 作者: 村田泰彦;菱田智大;吉田高平;所寛
• 通讯作者: 所寛

射出成形におけるバリ発生計測

注塑中毛刺产生的测量

• 发表时间: 2011
• 作者: 菱田智大;小松拓哉;村田泰彦;新田和男;齊藤一男;菊森一洋
• 通讯作者: 菊森一洋