Development of the antibacterial thermoplastic resin

抗菌热塑性树脂的开发

• 批准号: 23792258
• 负责人: SHIMPO Hidemasa
• 金额: $ 2.5万
• 依托单位: Tsurumi University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23792258/
• 关键词: 有床義歯補綴学; 抗菌性; 熱可塑性樹脂

This study was developed a new thermoplastic resin with the antibacterial. After added a 0.3-30.0% water-soluble silver ion into polyamide thermoplastic resin at a percent by weight, specimens were fabricated using multi injection-molded system. After, Candida albicans was perfomed aerobic culture at 37 degrees C using Sabouraud agar for 48 hours and, only except suspension bacteria, cultured it more for 32 hours. The residual probiotic quantity measured using fluorescence stain for 6-60 hours. These results indicated, depression effect of the bacteria was observedpolyamide thermoplastic resin with over 15.0 % of silver ion concentration 60 hours later.

本研究开发了一种具有抗菌作用的新型热塑性树脂。在聚酰胺热塑性树脂中按重量百分比添加0.3-30.0%的水溶性银离子后，采用多注射成型系统制造样品。然后，使用沙氏琼脂将白色念珠菌在37℃需氧培养48小时，仅除去悬浮菌，再培养32小时。使用荧光染色6-60小时测量残留益生菌数量。这些结果表明，银离子浓度超过15.0％的聚酰胺热塑性树脂在60小时后观察到细菌的抑制效果。

项目成果

抗菌性熱可塑性合成樹脂の開発

抗菌热塑性合成树脂的开发

• 发表时间: 2013
• 作者: Hiroshi Suzuki;Aito Watanabe;渡邊愛斗;渡邊 愛斗;渡邊愛斗;渡邊愛斗;渡邊 愛斗;新保秀仁 ,岡山章太郎,佐藤薪,大久保力廣,大島朋子,前田伸子
• 通讯作者: 新保秀仁 ,岡山章太郎,佐藤薪,大久保力廣,大島朋子,前田伸子

抗菌性熱可塑性樹脂の検討

抗菌热塑性树脂的研究

• 作者: Kitano N;Tokue A;Suzuki T;Shimpo H;Ohkubo C;新保秀仁
• 通讯作者: 新保秀仁

Metal based denture with thermoplastic resin clasps using new adhesive system

使用新型粘合系统的带有热塑性树脂扣环的金属基义齿

• 发表时间: 2011
• 作者: Shimpo H;Takahashi M;Chiba N;Kurihara D;Ohkubo C;Kenneth S. Kurtz
• 通讯作者: Kenneth S. Kurtz

Bonding strength of silicone soft relining materials to thermoplastic reksins

有机硅软衬里材料与热塑性树脂的粘合强度

• 发表时间: 2011
• 作者: Kitano N;Tokue A;Suzuki T;Shimpo H;Ohkubo C
• 通讯作者: Ohkubo C