Martensitic transformation and shape memory behavior of Ti-V-Al-Fe lightweight shape memory alloys
Martensitic transformation and shape memory behavior of Ti-V-Al-Fe lightweight shape memory alloys
复制标题
Ti-V-Al-Fe轻质形状记忆合金的马氏体相变和形状记忆行为
DOI：
10.1016/j.jallcom.2016.04.151
复制
发表时间：
2016-09
影响因子：
6.2
通讯作者：
Cai W.
中科院分区：
文献类型：
--
作者：
Yang Z. Y.;Zheng X. H.;Wu Y.;Cai W.
研究了添加Fe对Ti-V-Al-Fe合金马氏体相变和形状记忆行为的影响。微量Fe显著降低了Ti-V-Al合金的马氏体相变温度，增强了合金的形状记忆效应。Fe含量最佳的Ti-13V-3Al-1Fe合金在预应变为6%时，可恢复应变最大，为5.8%，最大恢复应力为250 Mpa。同时，Ti-13V-3Al-1Fe合金具有高达30%的延伸率。
Effects of Fe addition on martensitic transformation and shape memory behavior of Ti-V-Al-Fe alloys were investigated. A little amount of Fe addition reduces martensitic transformation temperature rapidly and enhances shape memory effect of Ti-V-Al alloy. Alloy with an optimal Fe content, which is Ti-13V-3Al-1Fe, shows the largest recoverable strain of 5.8% and highest recovery stress of 250 MPa when pre-strain is 6%. Meanwhile, Ti-13V-3Al-1Fe alloy has a large elongation of 30%.
登录
查看更多内容
DOI：
10.1201/9780849391088.ax2
发表时间：
2006-12
期刊：
--
影响因子：
--
作者：
V. Konchits
通讯作者：
V. Konchits
DOI：
10.1016/s0921-5093(00)00816-9
发表时间：
2000-07
影响因子：
6.4
作者：
P. Šittner;D. Vokoun;G. Dayananda;R. Stalmans
通讯作者：
P. Šittner;D. Vokoun;G. Dayananda;R. Stalmans
影响因子：
1.3
作者：
Xiaojun Yan;J. Humbeeck
通讯作者：
Xiaojun Yan;J. Humbeeck
影响因子：
2.3
作者：
M. González;J. Peña;J. Manero;M. Arciniegas;F. Gil
通讯作者：
M. González;J. Peña;J. Manero;M. Arciniegas;F. Gil
影响因子：
2.3
作者：
M. González;J. Peña;J. Manero;M. Arciniegas;F. Gil
通讯作者：
M. González;J. Peña;J. Manero;M. Arciniegas;F. Gil