Chromium-modified a-C films with advanced structural, mechanical and corrosive-resistant characteristics
Chromium-modified a-C films with advanced structural, mechanical and corrosive-resistant characteristics
复制标题
具有先进结构、机械和耐腐蚀特性的铬改性 a-C 薄膜
DOI：
10.1016/j.apsusc.2016.04.112
复制
发表时间：
2016-08
影响因子：
6.7
通讯作者：
Balmakou A.
中科院分区：
文献类型：
--
作者：
Ming Miao Yi;Jiang Xiaohong;Piliptsou D. G.;Zhuang Yuzhao;Rogachev A. V.;Rudenkov A. S.;Balmakou A.
为了改善类金刚石碳薄膜的结构、机械和化学性能，我们开发了采用阴极磁过滤电弧沉积法制备的非晶碳铬改性复合薄膜。通过拉曼光谱、X射线光电子能谱和原子力显微镜对其性能进行分析，以进行结构表征、元素分析和拓扑检查。此外，我们还通过X射线双晶表面轮廓测量、摩擦测试、纳米压头测试以及接触角测量和动电位极化分析来评估残余应力、摩擦系数、硬度、弹性模量和腐蚀参数。通过比较分析，我们发现与非晶碳薄膜相比，所开发的复合薄膜的特性有了显着改善。例如，Cr变质，综合性能、韧性和耐腐蚀性能得到提高；残余应力显着降低。
To improve structural, mechanical and chemical properties of diamond-like carbon films, we developed amorphous carbon chromium-modified compositefilms fabricated bymeans of cathodemagneticfiltered arc deposition. The properties were analyzed by Raman spectroscopy, X-ray photoelectron spectroscopy and atomic force microscopy for the purpose of the structure characterization, elemental analysis and topology examination. Moreover, we also assessed residual stress, the coefficient of friction, hardness, the elastic modulus and corrosion parameters through X-ray double-crystal surface profilometry, tribotesting, nanoindenter-testing, as well as contact angle measurements and potentiodynamic polarization analysis..As a result of a comparative analysis, we revealed a substantial improvement in the characteristics of developed composite films in comparison with amorphous carbon films. For example, Cr-modification is resulted, in greater integrated performance, toughness and corrosion resistance; the residual stress wasreduced substantially.
登录
查看更多内容
电化学阳极氧化形成的 SiGe 纳米晶的光学性质研究
影响因子：
6.7
作者：
Pan, S. W.;Zhou, Bi;Chen, S. Y.;Li, Cheng;Huang, Wei;Lai, H. K.
通讯作者：
Lai, H. K.
影响因子：
5.4
作者：
Bing Zhou;A. Rogachev;Zhubo Liu;Xiaohong Jiang;R. Shen;A. Rudenkov
通讯作者：
Bing Zhou;A. Rogachev;Zhubo Liu;Xiaohong Jiang;R. Shen;A. Rudenkov
影响因子：
2.1
作者：
Varshni Singh;Jiechao Jiang;E. Meletis
通讯作者：
Varshni Singh;Jiechao Jiang;E. Meletis
影响因子：
5.4
作者：
Sam Zhang;Deen Sun;Y. Fu;H. Du
通讯作者：
Sam Zhang;Deen Sun;Y. Fu;H. Du
影响因子：
4.1
作者：
A. Pardo;C. Gómez-Aleixandre;J. Orwa;A. Cimmino;S. Prawer
通讯作者：
A. Pardo;C. Gómez-Aleixandre;J. Orwa;A. Cimmino;S. Prawer