Temperature-dependent and polarization-tuned resistive switching in Au/BiFeO3/SrRuO3 junctions
Temperature-dependent and polarization-tuned resistive switching in Au/BiFeO3/SrRuO3 junctions
复制标题
Au/BiFeO3/SrRuO3 结中的温度相关和极化调谐电阻开关
DOI：
10.1063/1.4870813
复制
发表时间：
2014-04
影响因子：
4
通讯作者：
Liu, J. -M.
中科院分区：
文献类型：
--
作者：
Yan, Z. B.;Lu, X. B.;Lu, Z. X.;Zeng, M.;Chen, Y.;Gao, X. S.;Wan, J. G.;Dai, J. Y.;Liu, J. -M.
研究了Au/BiFeO 3/SrRuO 3结构在不同温度下的双极阻变与极化反转之间的关系。结果表明，随着温度的降低，Au/BiFeO 3和BiFeO 3/SrRuO 3结中极化引起的势垒变化减小。这解释了为什么电阻开关比随温度降低而降低，并给出证据表明，极化调制的电阻状态的Au/BiFeO 3/SrRuO 3结构。此外，当温度高于323 K时，氧空位迁移和载流子俘获/脱陷机制对该结构的阻变行为也起着重要作用.
The relationship between the bipolar resistive switching and the polarization reversal is investigated at various temperatures in the Au/BiFeO3/SrRuO3 structure. It is found that the polarization-induced barrier variation in the Au/BiFeO3 and BiFeO3/SrRuO3 junctions decreases with decreasing temperature. This explains why the resistance-switching ratio decreases with decreasing temperature below 323 K and gives evidence that the polarization modulates the resistance state of the Au/BiFeO3/SrRuO3 structure. Besides, the oxygen vacancies migration and/or the carrier trapping/detrapping mechanisms are also suggested to play a very important role in the resistive switching behavior in this structure as the temperature goes above 323 K.
登录
查看更多内容
影响因子：
2.7
作者：
Fang, X;Kobayashi, T
通讯作者：
Kobayashi, T
影响因子：
1.6
作者：
X. Zou;H. G. Ong;L. You;Weigang Chen;H. Ding;H. Funakubo;Lang Chen;Junling Wang
通讯作者：
X. Zou;H. G. Ong;L. You;Weigang Chen;H. Ding;H. Funakubo;Lang Chen;Junling Wang
影响因子：
10.8
作者：
Yuchao Yang;Shinhyun Choi;W. Lu
通讯作者：
Yuchao Yang;Shinhyun Choi;W. Lu
影响因子：
3.5
作者：
Gang Jian-Lei;Li Songlin;Liao Zhao-liang;Meng Yang;Liang Xuejin;Chen Dong-min
通讯作者：
Gang Jian-Lei;Li Songlin;Liao Zhao-liang;Meng Yang;Liang Xuejin;Chen Dong-min
影响因子：
8.6
作者：
Nian, Y. B.;Strozier, J.;Ignatiev, A.
通讯作者：
Ignatiev, A.