Charge-discharge properties of lead zirconate stannate titanate ceramics
Charge-discharge properties of lead zirconate stannate titanate ceramics
复制标题
锆锡钛酸铅陶瓷的充放电性能
DOI：
10.1063/1.3187778
复制
发表时间：
2009-08
影响因子：
3.2
通讯作者：
Cao, Fei
中科院分区：
文献类型：
--
作者：
He, Hongliang;Zhang, Hongling;Dong, Xianlin;Liu, Yusheng;Gu, Yan;Wang, Genshui;Chen, Xuefeng;Cao, Fei
通过直接测量电滞回线、直流偏置场下的介电常数以及不同充放电循环后的脉冲放电电流-时间曲线，研究了镧和铒掺杂锆锡钛酸铅陶瓷的充放电性能。结果发现，有没有显着的影响，这些性能的充放电循环。第一个脉冲电流峰值在40 kV/cm时达到1.8 kA，大部分存储电荷在500 ns内释放。这些结果表明，所获得的具有高能量密度的倾斜陶瓷可以承受数百次充放电循环，是非常有前途的脉冲电容器的应用。
The charge-discharge properties of lanthanum- and niobium-doped lead zirconate stannate titanate ceramics were investigated by directly measuring the hysteresis loops, dielectric constants under a dc bias field, and pulse discharge current-time curves after varying charge-discharge circulations. It was found that there was no significant effect of the charge-discharge circulation on these properties. The first pulse current peak reached 1.8 kA at 40 kV/cm, and most of the stored charge was released in 500 ns. These results show that the obtained slanted ceramics with high energy density can withstand hundreds of charge-discharge circulations and are very promising for pulse capacitor applications.
登录
查看更多内容
影响因子：
3.2
作者：
J. Tortai;N. Bonifaci;A. Denat;C. Trassy
通讯作者：
J. Tortai;N. Bonifaci;A. Denat;C. Trassy
影响因子：
3.2
作者：
W. Pan;C. Dam;Qiming Zhang;L. Cross
通讯作者：
W. Pan;C. Dam;Qiming Zhang;L. Cross
影响因子：
4
作者：
N. Karan;J. Saavedra-Arias;M. Pérez;Reji Thomas;R. Katiyar
通讯作者：
N. Karan;J. Saavedra-Arias;M. Pérez;Reji Thomas;R. Katiyar
DOI：
10.1111/j.1151-2916.1990.tb06513.x
发表时间：
1990-02-01
影响因子：
3.9
作者：
LOVE, GR
通讯作者：
LOVE, GR
影响因子：
4
作者：
Parui, Jayanta;Krupanidhi, S. B.
通讯作者：
Krupanidhi, S. B.