Non-destructive Neutron Surface Residual Stress Analysis
Non-destructive Neutron Surface Residual Stress Analysis
复制标题
无损中子表面残余应力分析
DOI：
10.1007/s10921-019-0617-2
复制
发表时间：
2019
影响因子：
2.8
通讯作者：
J. Šaroun
中科院分区：
文献类型：
--
作者：
J. Rebelo Kornmeier;M. Hofmann;W. M. Gan;J. Gibmeier;J. Šaroun
衍射是研究工程材料和构件中残余应力和外加应力的有力工具。X射线和中子衍射都可以用于此目的。对中子应力分析的兴趣源于与实验室X射线源相比中子的高穿透能力，即在金属材料中的几厘米而不是几十微米。本文概述了目前的仪器和方法的发展，通过非破坏性的表面应变测量，桥梁之间的差距X射线和中子分析差距。
Diffraction is a powerful tool for investigation of residual as well as applied stresses in engineering materials and components. Both X-ray and neutron diffraction can be used for this purpose. The interest in neutron stress analysis stems from the high penetrating power of neutrons when compared to laboratory X-ray sources, i.e. several cm instead of a few tens of µm in metallic materials. This contribution gives an overview on current instrumental and methodical developments for non-destructive through surface strain measurements, which bridges the gap between X-rays and neutrons analysis.
登录
查看更多内容
表面效应引起的中子衍射峰位移的分析模型
影响因子：
6.1
作者：
J. Šaroun;J. Rebelo Kornmeier;M. Hofmann;P. Mikula;M. Vrana
通讯作者：
M. Vrana
影响因子：
2.4
作者：
J. Rebelo Kornmeier;J. Gibmeier;M. Hofmann
通讯作者：
J. Rebelo Kornmeier;J. Gibmeier;M. Hofmann
影响因子：
1.1
作者：
Eigenmann, B;Macherauch, E
通讯作者：
Macherauch, E
DOI：
10.4028/www.scientific.net/msf.524-525.211
发表时间：
2006-01-01
期刊：
RESIDUAL STRESSES VII
影响因子：
--
作者：
Hofmann, M.;Seidl, G. A.;Noster, U.
通讯作者：
Noster, U.
界面处的中子应变扫描：减少表面效应的优化光束光学器件
DOI：
--
发表时间：
2000
期刊：
影响因子：
--
作者：
T. Pirling
通讯作者：
T. Pirling