In vitro degradation of AZ31 magnesium alloy coated with nano TiO2 film by sol–gel method
In vitro degradation of AZ31 magnesium alloy coated with nano TiO2 film by sol–gel method
复制标题
溶胶凝胶法体外降解纳米TiO2薄膜AZ31镁合金
DOI：
10.1016/j.apsusc.2011.03.148
复制
发表时间：
2011-08
影响因子：
6.7
通讯作者：
Shijie Zhu
中科院分区：
文献类型：
--
作者：
Junhua Hu;Caili Zhang;Baohong Cui;Kuifeng Bai;Shaokang Guan;Liguo Wang;Shijie Zhu
采用溶胶-凝胶法在AZ31合金基体上制备纳米TiO2薄膜。通过X射线衍射(XRD)、差示扫描量热-热重分析(DSC-TG)、场发射扫描电子显微镜(FE-SEM)和能量色散光谱(EDS)对TiO2薄膜进行了表征。通过浸泡试验和电化学测量评价纳米TiO2涂层合金的降解性能。尝试将涂层合金的腐蚀与退火处理和由此产生的结构演变联系起来。
A nano TiO2film was coated on AZ31 alloy substrate by sol–gel method. The TiO2film was characterized by X-ray diffractometry (XRD), differential scanning calorimetry-thermogravimetric analysis (DSC-TG), field emission scanning electron microscopy (FE-SEM) and energy dispersion spectroscopy (EDS). The degradation of the nano-TiO2coated alloy was evaluated by immersion test and electrochemical measurement. An attempt was made to relate corrosion of coated alloys with the annealing treatment and resultant structural evolution.
登录
查看更多内容
影响因子：
14
作者：
Xu, Liping;Pan, Feng;Yang, Ke
通讯作者：
Yang, Ke
影响因子：
44.1
作者：
CHILDS, BG
通讯作者：
CHILDS, BG
影响因子：
5.4
作者：
Y. Leng;N. Huang;P. Yang;Jun-ying Chen;Hong Sun;J. Wang;G. Wan;X. Tian;R. Fu;L. Wang;P. Chu
通讯作者：
Y. Leng;N. Huang;P. Yang;Jun-ying Chen;Hong Sun;J. Wang;G. Wan;X. Tian;R. Fu;L. Wang;P. Chu
影响因子：
4.5
作者：
Meiheng Li;Qian Chen;Wenjing Zhang;Wangyu Hu;Yong-liang Su
通讯作者：
Meiheng Li;Qian Chen;Wenjing Zhang;Wangyu Hu;Yong-liang Su
影响因子：
2.1
作者：
Legrand-Buscema, C;Malibert, C;Bach, S
通讯作者：
Bach, S