Effect of ZnAl2O4 content on the microstructure and electrical properties of ZnO-based compound conductive ceramics
Effect of ZnAl2O4 content on the microstructure and electrical properties of ZnO-based compound conductive ceramics
复制标题
ZnAl2O4含量对ZnO基复合导电陶瓷微观结构和电性能的影响
DOI：
10.1016/j.jallcom.2018.03.289
复制
发表时间：
2018-06
影响因子：
6.2
通讯作者：
Wang Fen
中科院分区：
文献类型：
--
作者：
Chen Minge;Liu Qian;Zhu Jianfeng;Wang Fen
ZnO-ZnAl2O4-SiO2-Y2O3-MgO conductive ceramics were fabricated with different amount of ZnAl2O4content. The effects of ZnAl2O4on the microstructures and electrical properties of ZnO-based compound conductive ceramics were investigated. Results showed that the continuously adjustable resistivity could be obtained under the percolation threshold through increasing ZnAl2O4content and improving the preparing technology. It was found that ZnAl2O4grain would be encased in the major ZnO grains, with less than 5.0 mol%. When more ZnAl2O4doping in the samples, it acted as a barrier blocking ZnO grain growth. Interestingly, the dielectric properties indicate that the Maxwell-Wagner interfacial polarization and the threshold effect exists in the matrixes. At the same time, the resistance-temperature (R-T) characteristics verify that the conduction mechanism of ZnO-based conductive compound ceramics is a thermally activated progress and the grain-boundary effect is negligible. The improvement of the microstructures and electrical properties has a potential application in the high frequency electrical fields.
登录
查看更多内容
DOI：
10.1007/s10854-013-1647-7
发表时间：
2014-02
期刊：
Journal of Materials Science: Materials in Electronics
影响因子：
--
作者：
Jianfeng Zhu;Jingjing Wang;Yong Zhou;Fen Wang
通讯作者：
Jianfeng Zhu;Jingjing Wang;Yong Zhou;Fen Wang
影响因子：
6.7
作者：
Prodromakis, T.;Papavassiliou, C.
通讯作者：
Papavassiliou, C.
影响因子：
3
作者：
Yongheng Zhang;Juan Han
通讯作者：
Yongheng Zhang;Juan Han
天然赤铁矿矿石与 ZnO 纳米针复合用于能源应用
DOI：
10.1016/j.compositesb.2017.11.020
发表时间：
2018-03
期刊：
Composites Part B: Engineering
影响因子：
--
作者：
Yan Wu;Liang Liu;Xinxin Yu;Jing Zhang;Lingyao Li;Chunjie Yan;Bin Zhu
通讯作者：
Bin Zhu
DOI：
10.1007/s10854-014-2018-8
发表时间：
2014-05
期刊：
Journal of Materials Science: Materials in Electronics
影响因子：
--
作者：
Jingjing Wang;Jianfeng Zhu;Yong Zhou;Fen Wang
通讯作者：
Jingjing Wang;Jianfeng Zhu;Yong Zhou;Fen Wang