Study of an arbitrary crystal orientation controlling method by a press process

通过压制工艺控制任意晶体取向方法的研究

• 批准号: 24656100
• 负责人: YOSHINO Masahiko
• 金额: $ 2.66万
• 依托单位: Tokyo Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-24656100/
• 关键词: プレス加工; 生産工学; 鉄鋼材料; 結晶方位制御; 静的再結晶; 剪断; 機械工作・生産工学; 金属生産工学; モーター; 鉄心; 結晶方位

The objective of this project is to study a new method to control crystal orientation of an iron sheet by using press machine. Firstly, an equipment to conduct experiments which adds vibration of shear stress to an iron sheet specimen was developed. After shear stress was added to a specimen many times by the equipment, the specimen was annealed. Then the distributions of crystal orientation were analyzed by an EBSD. It was found from the experiments that grains of particular crystal orientation was grown to be very large grains. Possibility of crystal orientation control was shown.

该项目的目的是研究一种使用压力机控制铁片晶体取向的新方法。首先，开发了一种向铁片试样施加剪切应力振动的实验设备。通过设备多次对试样施加剪切应力后，对试样进行退火。然后通过EBSD分析了晶体取向的分布。实验发现，特定晶体取向的晶粒生长成非常大的晶粒。显示了晶体取向控制的可能性。

项目成果

EBSD Analysis of Static Recrystallized Microstructure Formed by Nano Plastic Forming and Annealing

纳米塑性成形及退火静态再结晶显微组织的EBSD分析

• 发表时间: 2012
• 作者: Kohei Ibuki;Akinori Yamanaka;Masahiko Yoshino
• 通讯作者: Masahiko Yoshino

鉄板の組織変化に及ぼすせん断ひずみの影響

剪应变对钢板结构变化的影响

• 发表时间: 2013
• 作者: 藤野清次;阿部邦美;杉原正顯;中嶋徳正;廣澤勇二,寺野元規,吉野雅彦,鳥塚史郎
• 通讯作者: 廣澤勇二,寺野元規,吉野雅彦,鳥塚史郎

学術研究助成基金助成金（挑戦的萌芽研究）

学术研究资助基金资助（具有挑战性的探索性研究）