Development of green stainless steels by micro-and nano-scale surface design and control

通过微米和纳米级表面设计和控制开发绿色不锈钢

• 批准号: 20246106
• 负责人: HARA Nobuyoshi
• 金额: $ 31.37万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (A)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-20246106/
• 关键词: 腐食防食; ステンレス鋼; 耐酸性; 耐孔食性; 硫化物介在物; 微小部分電気化学計測; キャピラリーセル; アノード分極曲線; キャピラリ-セル

In order to develop a new passivation method for removing MnS from the surface of stainless steels and forming a Cr enriched passive film on the surface, microelectrochemical electrochemical properties of MnS and chemical dissolution behaviors of MnS in chelate-containing solutions have been examined. It was found that citric acid system solutions are effective to remove MnS and to improve corrosion resistance of stainless steels.

为了开发一种从不锈钢表面去除MnS并在表面形成富铬钝化膜的新的钝化方法，研究了MnS的微电化学性质和MnS在含螯合物溶液中的化学溶解行为。结果表明，柠檬酸体系溶液能有效去除不锈钢中的MnS，提高不锈钢的耐蚀性。

项目成果

Fe-10Cr合金の耐食性に及ぼすSi, Cu, N添加の効果のコンビナトリアル評価

Si、Cu、N添加对Fe-10Cr合金耐蚀性影响的组合评价

• 发表时间: 2009
• 作者: 榑林光一;武藤泉;原信義
• 通讯作者: 原信義

Microelectrochemical Investigation of Hydrogen Absorption and Dissolution Behavior of MnS Inclusions in Carbon Steel

• DOI: 10.1149/1.3577749
• 发表时间: 2011-04
• 作者: I. Muto;Junichi Shinozaki;T. Omura;M. Numata;N. Hara

MnS系介在物の化学的除去処理によるステンレス鋼表面の高耐食化

通过化学去除MnS系夹杂物处理，使不锈钢表面具有高耐腐蚀性

• 发表时间: 2010
• 作者: 原信義;滝沢友暁;武藤泉
• 通讯作者: 武藤泉

コンビナトリアルアプローチによる低Cr含有ステンレス合金の探索

使用组合方法探索低铬含量不锈钢合金

• 发表时间: 2008
• 作者: 滝沢友暁;武藤泉;原信義
• 通讯作者: 原信義

実不働態皮膜から人工不働態皮膜へ, そして再び実不働態皮膜へ

从真正的钝化膜到人造钝化膜，再回到真正的钝化膜

• 发表时间: 2010
• 期刊: 材料と環境
• 作者: O.Ciuca;K.Tsuchiya;Y.Yokoyama;Y.Todaka;M.Umemoto;大塚哲也・後藤治・吉澤政己;原信義
• 通讯作者: 原信義