Utilization of wasted carbon dioxide to cement lining method

废弃二氧化碳利用水泥衬砌方法

• 批准号: 06838009
• 负责人: SUZUKI Takeo
• 金额: $ 1.34万
• 依托单位: Hiroshima Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 1994
• 资助国家: 日本
• 起止时间: 1994 至 1996
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-06838009/
• 关键词: Cement lining method; Carbon dioxide; Early strength; unconfined compressive strength; tunnel; セメント吹付け工法; セメント; 吹付け工法; モルタル; セメントペースト; 短期強度発現; 温度上昇; 吹付け装置

In the lavolatory experiments, utilization of carbon dioxide to cement lining was studied to get early strength by the hydration of cement.In the change of cement lining condition, kinds of cement ; ordinary portland cement, high early portland cement, moderate portland cement, portland blast-furnace slag cement, water cement ratio : 27-60%, carbon dioxide concentration in the air ; 0-10%, the temperature of mixing water ; 10ﾟC-20ﾟC,curing time : 1hour-7days, the test pieces are made and tested by the unconfined compressive strength. Good test results were obtained at 40%-60% carbon dioxide concentration for each cements.By this research, that were found utilization of carbon dioxide to cement were very effective.

在室内试验中，研究了二氧化碳在水泥衬里中的应用，通过水泥的水化作用获得水泥的早期强度。在水泥衬砌条件变化时，水泥的种类；普通硅酸盐水泥、高早硅酸盐水泥、中硅酸盐水泥、硅酸盐高炉矿渣水泥，水灰比：27-60%，空气中二氧化碳浓度；0-10%，混水温度；10 C-20 C，固化时间：1小时-7天，试件制作并进行无侧限抗压强度试验。每种水泥在二氧化碳浓度为40% ~ 60%时均获得了良好的测试结果。通过本研究，我们发现二氧化碳在水泥中的利用是非常有效的。

项目成果

鈴木健夫・津村拓美: "二酸化炭素添加による粘性土の固化について" 材料学会シンポジウム. 2. 201-208 (1997)

Takeo Suzuki 和 Takumi Tsumura：“通过添加二氧化碳来固化粘性土壤”日本材料学会研讨会 2. 201-208 (1997)。

Takeo Suzuki, Takumi Tumura: "Utilization of carbon dioxide to clay and cement" Symposium of society of materials science Japan. No.2. 201-208 (1997)

Takeo Suzuki、Takumi Tumura：“二氧化碳在粘土和水泥中的利用”日本材料学会研讨会。

鈴木健夫・津村拓美: "二酸化炭素添加による粘性土の固結について" 第2回地盤改良シンポジウム発表論文集. 2. 201-208 (1997)

Takeo Suzuki 和 Takumi Tsumura：“通过添加二氧化碳来加固粘性土壤”第二届地面改良研讨会论文集 2. 201-208 (1997)。