Surface treatments of bone fixators consiting of titanium alloys to inhibit the formation of callus

钛合金骨固定器表面处理抑制骨痂形成

• 批准号: 18300160
• 负责人: HANAWA Takao
• 金额: $ 11.57万
• 依托单位: Tokyo Medical and Dental University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2006
• 资助国家: 日本
• 起止时间: 2006 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-18300160/
• 关键词: チタン; ジルコニウム; 骨形成; リン酸カルシウム; カソード分極; 表面分析; マイクロアーク酸化; チタン合金; 骨折固定材; 表面被覆; 不動態皮膜

Difference in the ability of calcium phosphate formation between Ti and Zr was caused by the difference in the stability of surface oxide films on both metals. Zr coating was effective to prevent calcium phosphate formation on Ti. On the other hand, cathodic polarization of Zr in a supporting electrolyte made it possible to add the ability of calcium phosphate formation to Zr and its mechanism was elucidated. Zr coating is effective to prevent the formation of callus on Ti alloys used for internal bone fixators.

钛和锆形成磷酸钙能力的差异是由于两种金属表面氧化膜稳定性的差异造成的。Zr涂层能有效防止钛表面形成磷酸钙。另一方面，Zr在支撑电解质中的阴极极化使Zr的磷酸钙生成能力得以增加，并阐明了其形成机理。Zr涂层可有效防止骨内固定物钛合金的骨痂形成。

项目成果

機能分子による金属の生体機能化

使用功能分子对金属进行生物功能化

• 发表时间: 2008
• 期刊: 軽金属 58
• 作者: Harada;Y.;Takamatsu;T;藤堂貴弘;Takahashi S. et al.;塙隆夫
• 通讯作者: 塙隆夫

カソード分極処理によるZrの硬組織適合性の改善

阴极极化处理提高Zr硬组织相容性

• 发表时间: 2010
• 作者: 堤祐介;森山義久;大家渓;土居壽;野村直之;野田和彦;塙隆夫
• 通讯作者: 塙隆夫

骨芽細胞様細胞の遺伝子発現の金属の種類による相違

成骨细胞样细胞中基因表达的差异取决于金属类型

• 发表时间: 2009
• 作者: 大家渓;竹村太郎;堤祐介;土居壽;野村直之;花方信孝;塙隆夫
• 通讯作者: 塙隆夫

カソード分極処理を施したZrの擬似体液中におけるリン酸カルシウム形成能評価

模拟体液中阴极极化Zr形成磷酸钙能力的评价

• 发表时间: 2009
• 作者: 森山義久;今井八郎;塙隆夫;野村直之;土居壽;堤祐介
• 通讯作者: 堤祐介

チタン, ジルコニウム, 金のMC3T3-E1細胞骨分化特性の差異

钛、锆、金MC3T3-E1细胞成骨分化特性的差异

• 发表时间: 2008
• 作者: 大家渓;坂本晴美;堤祐介;土居壽;塙隆夫
• 通讯作者: 塙隆夫