Application of Nanofioscience to Dentin Regenerative Theraysy

纳米科学在牙本质再生治疗中的应用

• 批准号: 19390484
• 负责人: YOSHIYAMA Masahiro
• 金额: $ 8.15万
• 依托单位: Okayama University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2007
• 资助国家: 日本
• 起止时间: 2007 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-19390484/
• 关键词: 保存修復学; 象牙質再生療法; EVA+C; 修復象牙質; EVA; ナノハイドロキシアパタイト; 脱灰象牙質; 象牙質; 引張り接着強さ; セルフェッチングプライマー; ナノ・ハイドロキシアパタイト

The mineralization accelerating adhesion materials that added EVA+C (RMSB) were produced experimentally, and we studied the bond strength and biocompatibility. Bond strength decreased with increase of the EVA+C addition ratio. The RMSB group showed a tendency to growth similar to Control at the early phase, and cell count was higher than an SB (Superbond) at high ratio of EVA+C group. SBP30 and 7P (SB/EVA+C=40wt%/60wt%) showed a high bond strength and a good cell proliferation. Invivo, 7P had weaker inflammation than an SB and mineralized tissue formation was good. High adhesive property and biocompatibility was oftained by RMSB-7P.

实验制备了添加伊娃+C（RMSB）的矿化促进粘接材料，并对其粘接强度和生物相容性进行了研究。随着伊娃+C添加比例的增加，粘接强度降低。RMSB组在早期阶段显示出与对照相似的生长趋势，并且细胞计数高于伊娃+C组的高比率的SB（Superbond）。SB 30和7 P（SB/伊娃+C= 40 wt %/60 wt %）表现出较高的结合强度和良好的细胞增殖能力。在体内，7 P的炎症比SB弱，矿化组织形成良好。RMSB-7 P具有良好的粘附性和生物相容性。

项目成果

骨髄間葉系幹細胞を用いた象牙芽細胞分化象牙質再生に関する研究

骨髓间充质干细胞成牙本质细胞分化及牙本质再生研究

• 发表时间: 2008
• 作者: 伊澤俊次、山路公造、西谷佳浩、吉山昌宏;他
• 通讯作者: 他

MI時代の歯科知識-プラークコントロールサイエンス & プラクティス-

MI时代的牙科知识 - 牙菌斑控制科学与实践 -

• 发表时间: 2009
• 作者: 吉山昌宏;他
• 通讯作者: 他

リコンビナントヒトBMP-2配合アレギン酸ゲルを用いた骨再生療法の開発

使用含有重组人 BMP-2 的 Allegic Acid 凝胶开发骨再生疗法

• 发表时间: 2007
• 作者: 山路公造;吉山昌宏
• 通讯作者: 吉山昌宏

接着性コンポジットレジン修復の基礎と臨床

粘合复合树脂修复体的基础知识和临床方面

• 发表时间: 2007
• 作者: 山田敏元、吉山昌宏;他
• 通讯作者: 他

コラーゲン固定化エチレン-ビニルアルコール共重合体( EVA+C )添加試作石灰化誘導促進性接着剤の接着強さと生体親和性に関する基礎的研究

胶原固定乙烯-乙烯醇共聚物（EVA+C）促钙化粘合剂原型粘合强度和生物相容性基础研究

• 发表时间: 2008
• 作者: 神農泰生、吉山昌宏;他
• 通讯作者: 他