The development and application of composite functional medical device using new biodegradable magnesium alloy

新型可生物降解镁合金复合功能医疗器械的开发与应用

• 批准号: 20390496
• 负责人: SHIMIZU Yoshinaka
• 金额: $ 11.56万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20390496/
• 关键词: マグネシウム合金; 生体吸収性; 骨形成; 動物実験; 生体吸収性材料; 培養実験; 生体内埋入; マイクロCT

To apply biodegradable magnesium alloy for medical device, its biocompatibility and absorption velocity were examined in vitro and in vivo. In vitro, elevated activity of alkaline phosphatase was confirmed in osteoblast by magnesium ion addition. Magnesium alloy revealed the relationship between the degradation velocity and amount of gas formation. There was no pathological change in skin and bone tissue around magnesium alloy. The newly bone formation around magnesium alloy implant was seen in vivo examination. The biocompatibility and bone formation of magnesium alloy were confirmed by these results.

为将可生物降解镁合金应用于医疗器械，对其生物相容性和体内吸收速度进行了研究。在体外，碱性磷酸酶活性升高证实成骨细胞镁离子的加入。镁合金的降解速率与气体生成量之间存在一定的关系。镁合金周围皮肤和骨组织无病理改变。体内观察发现镁合金种植体周围有新骨形成。这些结果证实了镁合金的生物相容性和骨形成。

项目成果

生体吸収性マグネシウム合金の生体内埋入試験による分解挙動観察

生物可吸收镁合金体内植入试验分解行为观察

• 发表时间: 2009
• 作者: 山本玲子;清水良央;白井暢子;向井敏司
• 通讯作者: 向井敏司

Osteogenesis by gradually expanding the interface between bone surface and periosteum enhanced by bone marrow stem cell administration in rabbit

兔骨髓干细胞给药增强骨表面和骨膜之间的界面逐渐扩大成骨

• 发表时间: 2010
• 期刊: Oral Surg Oral Med Oral Pathol Oral Radiol Endod
• 作者: Sato K;Haruyama N;Shimizu Y;et al
• 通讯作者: et al

生体吸収性マグネシウム合金の生体内動態に関する研究

生物可吸收镁合金的体内动力学研究

• 发表时间: 2008
• 作者: 清水良央;山本玲子;向井敏司;白井暢子;狩野充浩;岡山啓昌;金高弘恭;菊地正嘉
• 通讯作者: 菊地正嘉

マグネシウム合金の生体材料応用

镁合金生物材料应用

• 发表时间: 2008
• 作者: 清水良央;山本玲子;向井敏司;白井暢子;狩野充浩;千葉亜耶美;金高弘恭;菊地正嘉
• 通讯作者: 菊地正嘉