• 关键词: RBセラミックス; 摩耗; 複合材料; トライボロジー; 炭素; 摩擦; 粒子; 充填剤; 樹脂; 銅合金

In the present study, new thermoplastic resin composite materials and copper alloy composite materials filled with RB ceramics particles, which are hard porous carbon materials RB Ceramics made from rice bran, were developed. The thermoplastic resin/RB ceramics composites and copper alloy/RB ceramics composites showed low friction and high wear resistance as well as low aggression against mating surfaces. It was demonstrated that the copper alloy/RB ceramics composites are available as new pantograph slider materials for current collector of railway.

本研究开发了以米糠为原料制备的硬质多孔炭材料RB陶瓷，即RB陶瓷颗粒填充的新型热塑性树脂复合材料和铜合金复合材料。热塑性树脂/RB陶瓷复合材料和铜合金/RB陶瓷复合材料表现出低摩擦、高耐磨性和低对配合面的侵蚀性。结果表明，铜合金/RB陶瓷复合材料可作为铁路受流器的新型受电弓滑板材料。

项目成果

Ryota Ifuku and Kazuo Hokkirigawa, Analysis of microscopic wear mechanism of copper/carbon/rice bran ceramics composites

Ryota Ifuku和Kazuo Hokkirikawa，铜/碳/米糠陶瓷复合材料的微观磨损机理分析

• 发表时间: 2011
• 作者: Kei Shibata;Takeshi Yamaguchi;Tatsuhiro Urabe
• 通讯作者: Tatsuhiro Urabe

RBセラミックス粒子を充填したポリエーテルエーテルケトン樹脂の摩擦・摩耗特性

RB陶瓷颗粒填充聚醚醚酮树脂的摩擦磨损性能

• 发表时间: 2011
• 作者: 山口健;針生渉;堀切川一男
• 通讯作者: 堀切川一男

銅/炭素/RBセラミックス複合材料の摩擦・摩耗に及ぼす接触圧力の影響

接触压力对铜/碳/RB陶瓷复合材料摩擦磨损的影响

• 发表时间: 2010
• 作者: 柴田圭;山口健;浦部達広;横山信行;堀切川一男
• 通讯作者: 堀切川一男

Friction and wear properties of PEEK composites filled with RB ceramics particles

RB陶瓷颗粒填充PEEK复合材料的摩擦磨损性能

• 发表时间: 2011
• 作者: Takeshi Yamaguchi;Sohei Nishio;Wataru Haryu;Kazuo Hokkirigawa
• 通讯作者: Kazuo Hokkirigawa

EBセラミックス粒子充填による熱可塑性樹脂の耐摩耗性発現メカニズムに関する研究

EB陶瓷颗粒填充热塑性树脂耐磨性能机理研究

• 发表时间: 2011
• 作者: 柴田圭;浦部達広;山口健;堀切川一男
• 通讯作者: 堀切川一男