This study developed a new powder processing which starts from liquid citrate precursors, and succeeded in a complex ferroelectric domain characterization, which resulted in the engineering of controlled grain-size distribution in alkali niobate ceramics. These facts were emphasized to prepare highperformance alkali niobate ceramics toward future industrial application.

本研究开发了一种从液态柠檬酸盐前驱体出发的新的粉末工艺，并成功地进行了复杂的铁电域表征，从而导致了碱式Nb酸盐陶瓷中可控粒度分布的工程化。为今后工业应用制备高性能的碱式铌酸盐陶瓷奠定了基础。

项目成果

Thermal Discharge Current Measurement for (Na, K)NbO_3 Piezoceramics

(Na,K)NbO_3 压电陶瓷的热放电电流测量

• 发表时间: 2010
• 作者: H.Matsudo;K.Kakimoto;I.Kagomiya
• 通讯作者: I.Kagomiya

Li/Na/K Ratio Dependence on Microstructure and Electrical Properties of Lead-free (Li, Na, K)NbO_3 Ceramics by Citrate Complex Process

柠檬酸盐复合法无铅(Li,Na,K)NbO_3陶瓷的Li/Na/K比对微观结构和电性能的依赖性

• 发表时间: 2010
• 作者: L.T.K.Nguyen;et al.
• 通讯作者: et al.

ニオブ系圧電材料の脱分極現象

铌基压电材料的去极化现象

• 发表时间: 2009
• 作者: 松堂人士;他
• 通讯作者: 他

(Li, Na, K)NbO_3無鉛圧電セラミックスの高圧ラマン分光測定

(Li,Na,K)NbO_3无铅压电陶瓷的高压拉曼光谱测量

• 发表时间: 2009
• 作者: 柿本健一;他
• 通讯作者: 他

Morphology-controlled Synthesis of KNbO_3 Particles using Plate-like KNb_3O_8 Precursor

使用板状 KNb_3O_8 前驱体形貌控制合成 KNbO_3 颗粒

• 发表时间: 2010
• 作者: K.Sugiyama;et al.
• 通讯作者: et al.