Development of bonding material inducing dentin remineralization

诱导牙本质再矿化的粘结材料的开发

• 批准号: 21791859
• 负责人: ITO Shuichi
• 金额: $ 2.91万
• 依托单位: Health Sciences University of Hokkaido
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21791859/
• 关键词: 歯学; 象牙質; 再石灰化; ボンディング材; 生体材料

In mineral induction experiments in vitro, the newly developed monomer, CMET, induced hydroxyapatite formation more rapidly than the model decalcified dentin matrix(PV). In the micro-tensile bond test, 4-META/MMA-TBB resin containing the newly developed monomers, CMET and CMEP at a concentration of 5 and 10% showed a high adhesive ability, equal to 4-META/MMA-TBB resin alone as a control. However, bond strength decreased significantly with the increase of the concentration.

在体外矿物质诱导实验中，新开发的单体CMET比模型脱钙牙本质基质（PV）更快地诱导羟基磷灰石形成。在微拉伸粘结试验中，含有浓度为5%和10%的新开发的单体CMET和CMEP的4-Meta/MMA-TBB树脂显示出高的粘合能力，与作为对照的单独的4-Meta/MMA-TBB树脂相等。但随着浓度的增加，粘结强度显著下降。

项目成果

Water sorption/solubility of self-etching dentin bonding agents

• DOI: 10.1016/j.dental.2010.03.001
• 发表时间: 2010-07-01
• 期刊: DENTAL MATERIALS
• 影响因子: 5
• 作者: Ito, Shuichi;Hoshino, Tomohiro;Saito, Takashi
• 通讯作者: Saito, Takashi

新規接着性モノマーCMET配合シーリングコート材の象牙質接着性及び再石灰化誘導能

含新型粘合单体CMET封闭层材料的牙本质粘合力及再矿化诱导能力

• 发表时间: 2011
• 作者: 甕富美子;伊藤修一;塚本尚弘;斎藤隆史
• 通讯作者: 斎藤隆史

Effects of several ions released from surface pre-reacted glass-ionomer fillers on dentin remineralization

表面预反应玻璃离聚物填料释放的几种离子对牙本质再矿化的影响

• 发表时间: 2011
• 作者: Ito S;Motai F;Saito T.
• 通讯作者: Saito T.

バイオアクティブ材料による象牙質再石灰化

使用生物活性材料进行牙本质再矿化

• 发表时间: 2010
• 作者: Hirata S;Fukushima H;Morotomi T;Aoki K;Nagano K;Ohya K;Kitamura C;Terashita M;Jimi E;伊藤修一
• 通讯作者: 伊藤修一

Effects of fluoride ions released from materials on dentin remineralization

材料释放的氟离子对牙本质再矿化的影响

• 发表时间: 2011
• 作者: Ito S;Iijima M;Mizoguchi I;Saito T.
• 通讯作者: Saito T.