Preparation of Transition Metal Oxide/Au small particle optical thin films by Wet proces

湿法制备过渡金属氧化物/Au小颗粒光学薄膜

• 批准号: 08650983
• 负责人: YOSHINO Takako
• 金额: $ 1.34万
• 依托单位: TOKYO METROPOLITAN UNIVERSITY
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 1996
• 资助国家: 日本
• 起止时间: 1996 至 1997
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-08650983/
• 关键词: nanocomposite; surface plasmon; Au small particle; optical device; electrodeposition

ZnO/Au nanocomposite thin films were fabricated by electrodepositon from an aqueous solution of Zn(NO_3)_2 and KAuCl_4. The composite film contained small particle of Au average diameter of which was in the range from 18 to 25 nm. The composite films was transparent and showed red color arise from the surface plasmon absorption of Au small particles as being deposited without subsequent heat treatment.

在Zn(NO_3)_2和KAuCl_4的水溶液中采用电沉积法制备了ZnO/Au纳米复合薄膜。复合膜中含有细小的Au颗粒，平均直径在18 ~ 25 nm之间。复合膜呈透明状，由于表面等离子体吸收Au小颗粒而未进行后续热处理而呈现红色。

项目成果

Takako YOSHINO: "Preparation of ZnO/Au Nanocomposite Thin Films by Electrodeposition" Jpn.J.Appl.Phys.Vol.35. L1512-L1514 (1996)

Takako YOSHINO：“通过电镀制备 ZnO/Au 纳米复合薄膜”Jpn.J.Appl.Phys.Vol.35。

Takako YOSHINO: "Electrolytic Synthesis of Hydrated IrOx Thin Films and Their Electrochromic Properties" Surface Fin.Soc.Jpn. Vol.47. 985-986 (1996)

Takako YOSHINO：“水合 IrOx 薄膜的电解合成及其电致变色性能”Surface Fin.Soc.Jpn。

吉野 隆子: "電解法によるECD用イリジウム酸化物薄膜の作製" 表面技術. Vol.49. 20-24 (1998)

Takako Yoshino：“电解法制备用于 ECD 的氧化铱薄膜”Surface Technology Vol.49（1998）。

Takao YOSHINO,Susumu TAKANEZAWA,Takashi OHMORI and Hideki MASUDA: "Preparation of ZnO/Au Nanocomposite Thin Films by Electrodeposition" Jpn.J.Appl.Phys.Vol.35, Part.2, No.11B. L1512-L1514 (1996)

Takao YOSHINO、Susumu TAKANEZAWA、Takashi OHMORI 和 Hideki MASUDA：“通过电镀制备 ZnO/Au 纳米复合薄膜” Jpn.J.Appl.Phys.Vol.35，第 2 部分，第 11B 号。

吉野隆子: "電解法によるECD用イリジウム酸化物薄膜の作製" 表面技術. Vol.9. 20-24 (1998)

Takako Yoshino：“电解法制备用于 ECD 的氧化铱薄膜”Surface Technology 第 20-24 卷（1998 年）。