Development of titanium dioxide/ clay mineral composites as a high functional photocatalyst

二氧化钛/粘土矿物复合材料作为高功能光催化剂的开发

• 批准号: 22550181
• 负责人: SUYAMA Yoko
• 金额: $ 3.08万
• 依托单位: Shimane University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22550181/
• 关键词: 光触媒; 二酸化チタン; ハイブリッド材料; 粘土鉱物; セピオライト; ナノ粒子; 環境材料; 光触媒材料

The novel TiO2/sepiolite composites were prepared from two kinds of sepiolite powders with different fibrous length and 0.05~0.2wt% of TiO2 sol. The preparation process of the composites was established by investigating the raw materials and the preparation conditions. The TiO2/sepiolite composites were found to possess a very high photocatalytic activity for the decomposition of dyes, formic acid and NOx under UV irradiation. A small-scale model of water purifying apparatus was fabricated by using the TiO2/sepiolite composites and UV light or LED light. The photocatalytic activity of the apparatus was investigated to evaluate the effect of the light source.

以两种纤维长度不同的海泡石粉为原料，添加0.05~0.2wt%的TiO2溶胶，制备了新型TiO2/海泡石复合材料。通过对原料和制备条件的研究，确定了复合材料的制备工艺。在紫外照射下，TiO2/海泡石复合材料对染料、甲酸和NOx的分解具有很高的光催化活性。采用TiO2/海泡石复合材料和紫外灯或LED灯制备了小型净水装置模型。研究了该装置的光催化活性，以评价光源的影响。

项目成果

TiO2繊維のメチルオレンジに対する光触媒作用

TiO2纤维对甲基橙的光催化作用

• 发表时间: 2011
• 作者: 清田諭史;陶山容子
• 通讯作者: 陶山容子

Photocatalytic activity of TiO2 thin films on glass beads

玻璃珠上TiO2薄膜的光催化活性

• 发表时间: 2011
• 作者: 中野智志、山脇浩;他;伊崎昌伸;Y.Suyama
• 通讯作者: Y.Suyama

Adsorption removal of lead and cadmium ions from aqueous solution with coal fly ash-derived zeollte/sepiolite composite

粉煤灰沸石/海泡石复合材料吸附去除水溶液中的铅和镉离子

• 发表时间: 2010
• 期刊: J.Ceram.Soc.Jpn.
• 作者: F.Miyaji;S.Masuda;Y.Suyama
• 通讯作者: Y.Suyama

TiO2/セピオライト複合材の光触媒効果

TiO2/海泡石复合材料的光催化效应

• 发表时间: 2011
• 作者: 根木洋平;陶山容子
• 通讯作者: 陶山容子

Degradation of Methyl Orange by TiO2 fibers

TiO2纤维降解甲基橙

• 发表时间: 2011
• 作者: S.Kiyota;Y.Suyama
• 通讯作者: Y.Suyama