Synthesis of Transparent Multifunctional Ceramics by Fast Densification Process

快速致密化合成透明多功能陶瓷

• 批准号: 24655186
• 负责人: ITO Akihiko
• 金额: $ 1.33万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-24655186/
• 关键词: 透明セラミックス; 蛍石型結晶構造; イオン伝導体; パイロクロア; 放電プラズマ焼結

A novel synthesis route to obtain transparent multifunctional ceramics by using SPS has been proposed. Transparent lutetium niobate (Lu3NbO7) had a cubic defect-fluorite structure, where Lu and Nb cations randomly occupy the 4a site, and 1/8 of the 8c site for O anion is statistically defective. Such disordering of cations and O defects makes Lu3NbO7 is an interesting multifunctional material. Transparent Lu3NbO7 ceramics had a uniform microstructure and the transmittance at 550 nm reached at 68%. TEM observation suggests the formation of ordered structure in Lu3NbO7 ceramics.

提出了一种利用SPS合成透明多功能陶瓷的新方法。透明的铌酸镥（Lu_3NbO_7）具有立方缺陷-萤石结构，其中Lu和Nb离子随机占据4a位，O阴离子占据8 c位的1/8统计缺陷。这种无序的阳离子和O缺陷使得Lu 3 NbO 7是一种有趣的多功能材料。结果表明，制备的Lu 3 NbO 7透明陶瓷具有均匀的显微结构，在550 nm处的透过率达到68%。透射电镜观察表明，在Lu_3NbO_7陶瓷的有序结构的形成。

项目成果

Scintillation Properties of Nd3+-doped Lu2O3 Transparent Ceramic in the Infra-red Region

Nd3掺杂Lu2O3透明陶瓷的红外区闪烁特性

• 发表时间: 2013
• 作者: Shunsuke Kurosawa;Akihiro Yamaji;Akira Suzuki;Yuui Yokota;Kenji Shirasaki;Yamamura Tomoo;Akihiko Ito;Takashi Goto;Georges Boulon and Akira Yoshikawa
• 通讯作者: Georges Boulon and Akira Yoshikawa

Scintillation properties of Nd^<3+>-doped Lu_2O_3 ceramics in the visible and infrared regions

Nd^<3>掺杂Lu_2O_3陶瓷的可见光和红外区闪烁特性

• 发表时间: 2014
• 期刊: IEEE Trans. Nucl. Sci
• 作者: S. Kurosawa;L. An;A. Yamaji;A. Suzuki;Y. Yokota;K. Shirasaki;T. Yamamura;A. Ito;T. Goto;G. Boulon;A. Yoshikawa
• 通讯作者: A. Yoshikawa

Transparent Luthetium oxides prepared by SPS

SPS 制备透明氧化钚

• 发表时间: 2013
• 作者: A. Ito;L. An;T. Goto
• 通讯作者: T. Goto

Scintillation Properties of Nd3+-Doped Lu2O3 Ceramic in the Visible and Infrared Regions

掺Nd3 Lu2O3陶瓷的可见光和红外区闪烁性能

• DOI: 10.1109/tns.2013.2290554
• 发表时间: 2014
• 期刊: IEEE Transactions on Nuclear Science
• 影响因子: 1.8
• 作者: Shunsuke Kurosawa;Liqiong An;Akihiro Yamaji;Akira Suzuki;Yuui Yokota;Kenji Shirasaki;Yamamura Tomoo;Akihiko Ito;Takashi Goto;Georges Boulon and Akira Yoshikawa
• 通讯作者: Georges Boulon and Akira Yoshikawa

Transparent Lu3NbO7 bodies prepared by reactive spark plasma sintering and their optical and mechanical properties

• DOI: 10.1016/j.ceramint.2012.06.038
• 发表时间: 2013
• 期刊: Ceramics International
• 影响因子: 5.2
• 作者: L. An;A. Ito;T. Goto