Innovative purivication of silicon using liquid phase migration in solid silicon

利用固体硅中的液相迁移进行硅的创新提纯

• 批准号: 24656455
• 负责人: YOSHIKAWA Takeshi
• 金额: $ 2.58万
• 依托单位: The University of Tokyo
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-24656455/
• 关键词: 太陽電池用シリコン; マイグレーション; 不純物液相

To develop the innovative solar cell silicon production, we conducted the following fundamental investigation on the liquid phase migration technique to selectively extract the impurity-concentrated phases in solid silicon.Thermodynamic analysis was carried out to clarify the purification effect of the migration process, and revealed the decrease the contents of impurity elements excluding P, B, Al and Fe to below 1 ppmw.Then, silicon sample was subjected to the heat treatment at 1523-1623 K under the temperature gradient. The migration velocity was increased by increasing temperature, and attained 50 µm/min at 1623 K. We found the sufficiently high migration velocity for purification process.

为了开发创新的太阳能电池硅生产，我们对液相迁移技术进行了以下基础研究，以选择性地提取固体硅中的杂质集中相。通过热力学分析，阐明了迁移过程的净化效果，并揭示了除P、B、Al和Fe之外的杂质元素含量降低到1 ppmw以下。然后，在1523-1623 K温度梯度下对硅样品进行热处理。迁移速度随温度的升高而增加，在1623 K时达到50 µm/min。我们发现足够高的迁移速度的纯化过程。

项目成果

Solar Grade Silicon Purification Using Liquid Phase Migration Technique

使用液相迁移技术提纯太阳能级硅

• 发表时间: 2013
• 作者: Kunitoshi Matsunaga;Takeshi Yoshikawa;Kazuki Morita
• 通讯作者: Kazuki Morita

固体Si中不純物液相のマイグレーション挙動の調査

固体硅中杂质液相迁移行为的研究

• 发表时间: 2013
• 作者: 松永邦俊;吉川健;森田一樹
• 通讯作者: 森田一樹

Purification of Silicon by Using the Liquid Migration Technique under Temperature Gradient

温度梯度下液体迁移技术提纯硅

• 发表时间: 2013
• 期刊: Materials Science Forum
• 作者: Kunitoshi Matsunaga;Takeshi Yoshikawa;Kazuki Morita
• 通讯作者: Kazuki Morita