Fabrication of anodic porous alumina with reduced hole interval and its application for the high-density magnetic recording media

缩小孔距阳极多孔氧化铝的制备及其在高密度磁记录介质中的应用

• 批准号: 21245048
• 负责人: MASUDA Hideki
• 金额: $ 30.04万
• 依托单位: Tokyo Metropolitan University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (A)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-21245048/
• 关键词: 高密度磁気記録媒体; パターンドメディア; 強磁性体

We studied formation of highly ordered anodic porous alumina with fine interval. As a result, we found anodizing conditions for forming highly ordered porous alumina with interval less than 25 nm. Ferromagnetic Co was electrochemically deposited in nanoholes of the porous alumina. Then, surface of the sample was flattened by dry etching or mechanical polishing. It was confirmed by Vibrating Sample Magnetometer measurement that the sample shows high squareness ratio(～0. 95) by control of the structure of Co/alumina nanocomposite.

研究了具有微细间距的高度有序阳极多孔氧化铝的形成。结果，我们发现阳极氧化条件形成高度有序的多孔氧化铝与间隔小于25纳米。在多孔氧化铝的纳米孔中电化学沉积铁磁Co。然后，通过干法蚀刻或机械抛光使样品的表面平坦化。通过振动样品磁强计的测量，证实了样品具有高的矩形比（~0。95)通过控制Co/Al_2O_3纳米复合材料的结构，

项目成果

背面冷却システムにもとづく陽極酸化ポーラスアルミナ化成条件の拡大

基于背面冷却系统的阳极氧化多孔氧化铝形成条件的扩展

• 发表时间: 2010
• 作者: 岡部都子;水木一成;柳下崇;西尾和之;益田秀樹
• 通讯作者: 益田秀樹

アノード酸化にもとづく規則ナノ構造の形成と機能的応用

基于阳极氧化的有序纳米结构的形成及其功能应用

• 发表时间: 2012
• 作者: D. Miyoshi;K. Nakamura;H. T. Karimata;T. Ohmichi;and N. Sugimoto;真島和志;益田秀樹
• 通讯作者: 益田秀樹

背面冷却システムにもとづくAlの高電流陽極酸化の安定化

基于背面冷却系统的铝大电流阳极氧化稳定性

• 发表时间: 2010
• 作者: 岡部都子;水木一成;柳下崇;西尾和之;益田秀樹
• 通讯作者: 益田秀樹

アルミナナノホールアレーにもとづく微細加工プロセス

基于氧化铝纳米孔阵列的微细加工工艺

• 发表时间: 2009
• 作者: 藤本健史;三好大輔;中野修一;杉本直己;下崇,益田秀樹
• 通讯作者: 下崇,益田秀樹

ナノインプリントプロセスにもとづくアノード酸プロセスの制御

基于纳米压印工艺的阳极酸过程控制

• 发表时间: 2010
• 作者: 小司禎教・國井勝・斉藤和雄;柳下崇,成山哲平,西尾和之,益田秀樹
• 通讯作者: 柳下崇,成山哲平,西尾和之,益田秀樹