Synthesis of Asymmetric Thermosensitive Multi-Layer Gels and Their Bending Behavior

不对称热敏多层凝胶的合成及其弯曲行为

• 批准号: 20550189
• 负责人: IIZAWA Takashi
• 金额: $ 3.24万
• 依托单位: Hiroshima University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20550189/
• 关键词: 感温性ゲル; 高分子反応; 多層ゲル; 屈曲性; LCST(下部臨界溶液温度)

A novel multi-layer gel containing different poly(N-alkyllacrylamide) was prepared by multi-step amidation of poly(acrylic acid) DBU salt with alkylamines. The asymmetric gels containing an intermediated layer or a graded composition between the core and the shell were bent markedly in response to the temperature changes. The shell layer did not peel off when the stepwise temperature changes were repeated.

通过聚丙烯酸DBU盐与烷基胺的多步酰胺化反应，制备了一种含不同聚N-烷基丙烯酰胺的多层凝胶。在核与壳之间含有中间层或梯度组成的不对称凝胶对温度变化的响应明显弯曲。壳层没有剥离时，逐步温度变化重复。

项目成果

「コアシェル微粒子の設計・合成技術・応用の展開」第5章「高分子反応を用いたコアシェル微粒子の合成」

“核壳微粒的设计、合成技术及应用的开发”第5章“利用聚合物反应合成核壳微粒”

• 发表时间: 2010
• 作者: 川口春馬;監修
• 通讯作者: 監修

Preparation of asymmetric thermosensitive double-layer gel

不对称热敏双层凝胶的制备

• 发表时间: 2007
• 作者: T. Iizawa;et. al.
• 通讯作者: et. al.

感温性IPN二層ゲルめ合成とその屈曲特性

温敏IPN双层凝胶的合成及其弯曲性能

• 发表时间: 2010
• 作者: 飯澤孝司;高橋智洋
• 通讯作者: 高橋智洋

Synthesis of Symmetric and Asymmetric Multi-Layer Gels Consisting of Different Poly (N-alkylacrylamide) Layers and Their Thermosensitive Behavior

不同聚N-烷基丙烯酰胺层的对称和不对称多层凝胶的合成及其热敏行为

• 发表时间: 2010
• 作者: Takashi Iizawa;Akihiro Terada
• 通讯作者: Akihiro Terada

Synthesis of Symmetric and Asymmetric Multi-Layer Gels Consisting of Different Poly(N-alkylacrylamide)Layers and Their Thermosensitive Behavior

不同聚N-烷基丙烯酰胺层的对称和不对称多层凝胶的合成及其热敏行为

• 发表时间: 2010
• 作者: Takashi Iizawa;Akihiro Terada
• 通讯作者: Akihiro Terada