Preparation of nanoparticle recording media for next-generation magnetic recording

下一代磁记录用纳米颗粒记录介质的制备

• 批准号: 21560348
• 负责人: ISHII Kiyoshi
• 金额: $ 3万
• 依托单位: Utsunomiya University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560348/
• 关键词: 磁気記録媒体; 垂直磁気記録媒体; スパッタ膜; ガスフロースパッタ法; FePt; 垂直磁気記録

In this study, we aimed at the development of nanoparticle magnetic recording media for next-generation recording media. For the purpose, a new sputtering method was used to prepare a FePt alloy thin film having the structures of L10 crystal phase and nanoparticle-assembly. As a result, we found that the FePt thin films with aimed structures and magnetic properties have been grown at the substrate temperature of about 300 ℃. They are considered as a thin film having very high potential as a nanoparticle magnetic recording medium.

在这项研究中，我们的目标是开发下一代记录介质的纳米颗粒磁记录介质。为此，使用一种新的溅射方法来制备具有L10晶相和纳米颗粒组装结构的FePt合金薄膜。结果表明，在300 ℃左右的衬底温度下，可以生长出具有目标结构和磁性的FePt薄膜。它们被认为是作为纳米颗粒磁记录介质具有非常高潜力的薄膜。

项目成果

Microstructure and magnetic properties of Co-doped ZnO films deposited by gas flow sputtering

气流溅射Co掺杂ZnO薄膜的微观结构和磁性能

• 发表时间: 2010
• 期刊: Materials Science & Engineering B (印刷中)
• 作者: Hiroshi Sakuma;他
• 通讯作者: 他

新しい強磁性Fe-As金属間化合物

新型铁磁铁砷金属间化合物

• 发表时间: 2011
• 作者: 鈴木涼;他
• 通讯作者: 他

ガスフロースパッタ法による新奇形状Fe微粒子の作製

气流溅射法制备新型铁颗粒

• 发表时间: 2010
• 作者: T.Mizuno;M.Hasegawa;T.Sameshima;齋藤勇介,坂本真一,佐久間洋志,石井清
• 通讯作者: 齋藤勇介,坂本真一,佐久間洋志,石井清

ガスフロースパッタ法によるFe 30 4のGaAs上へのエピタキシャル成長

气流溅射法在GaAs上外延生长Fe 30 4

• 发表时间: 2010
• 作者: 佐久間洋志;他
• 通讯作者: 他

新規磁性微粒子を用いた腫瘍細胞破壊方法

使用新型磁性粒子破坏肿瘤细胞的方法

• 发表时间: 2009
• 作者: 佐久間洋志;他
• 通讯作者: 他