Study on the processes of thin film preparation using nano-sized metal oxides for environmental usage

环境利用纳米金属氧化物薄膜制备工艺研究

• 批准号: 21560742
• 负责人: TANAKA Katsumi
• 金额: $ 2.91万
• 依托单位: The University of Electro-Communications
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560742/
• 关键词: 環境; ナノ微粒子; 薄膜作製; 作製プロセス; 酸化物; 可視光応答; 水中パルスレーザーアブレーション

The objective of the present study was to prepare uniform thin films at low temperature, for instance r. t., made of nano-particles with some functions for environmental cleanup. The TiO2 nanoparticles with N atoms, thermally stable up to 500℃, could be prepared in the pulsed laser ablation(PLA) in water with N atom involved acid or base. It was found that the uniform thin films could be obtained at r. t. by fabricating the nanoparticles prepared in the PLA in diluted ammonia solution. As the way to low temperature thin film preparation method is developed, one can continue to expand this field of technology.

本研究的目的是在低温下制备均匀的薄膜，例如在室温下。t.，由纳米颗粒制成，具有一定的环境净化功能。利用脉冲激光烧蚀法（PLA），在含有N原子的酸碱介质中制备了热稳定性达500℃的含N原子的TiO2纳米粒子。结果表明，在室温下可以得到均匀的薄膜. t.通过在稀氨溶液中制备PLA中制备的纳米颗粒。随着低温薄膜制备方法的发展，人们可以继续扩大这一技术领域。

项目成果

光触媒材料および製造方法

光催化材料及其制造方法

• 发表时间: 2010

光触媒材料およびその製造方法

光催化材料及其制备方法

• 发表时间: 2009

Bi系複合酸化物の作製と光触媒評価

铋基复合氧化物的制备及光催化评价

• 发表时间: 2010
• 作者: 戸水謙治;永井豊;チュウチャオキョン;田中勝己
• 通讯作者: 田中勝己

液相PLA法によるTiNからのTiO2微粒子の作製と評価

液相PLA法制备TiN TiO2颗粒并评价

• 发表时间: 2012
• 作者: 大高正嗣;Cheow Keong Choo;永井豊;田中勝己
• 通讯作者: 田中勝己

液相レーザーアブレーションで作製したTiO2微粒子の光触媒活性

液相激光烧蚀制备TiO2颗粒的光催化活性

• 发表时间: 2010
• 作者: 戸松靖博;チュウチャオキョン;永井豊;田中勝己
• 通讯作者: 田中勝己