Effects of adhesive strength on the fire resistance of glued laminated timber and development of an alternative test method for full-scale fire test

粘合强度对胶合层压木材耐火性的影响以及全尺寸耐火试验替代试验方法的开发

• 批准号: 22380100
• 负责人: HARADA Toshiro
• 金额: $ 11.98万
• 依托单位: Forestry and Forest Products Research Institute
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22380100/
• 关键词: 接着; 木質材料; 構造用集成材; 接着剤; 接着強度; 耐火性能; 炭化深さ; 簡易評価法

The fire resistance degradation of glued laminated timber (GLT) beams is dominated by the loss of laminae, and depends on the adhesive shear strength in laminated wood. If the adhesive shear strength at 200℃ is enough to keep laminae from separating, the GLT beam specimens are expected to exhibit 45-minute quasi-fireproof performance. Adhesive shear strength test at 200℃ can be an alternative test method for full-scale fire test.

胶合木（GLT）梁的耐火性能退化主要是由层板的损失引起的，并取决于胶合木中的胶合剪切强度。如果200℃时粘结剂的剪切强度足以防止层间剥离，则GLT梁试件有望表现出45分钟的准耐火性能。200℃胶粘剂剪切强度试验可作为全尺寸火灾试验的替代试验方法。