Challenge to evaluation of internal stress for materials with coarse grains

粗晶材料内应力评估的挑战

• 批准号: 24656083
• 负责人: SUZUKI Kenji
• 金额: $ 2.5万
• 依托单位: Niigata University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-24656083/
• 关键词: 残留応力; 粗大粒; 溶接材; シンクロトロン放射光; 回折斑点追跡法; 放射光Ｘ線; 内部応力測定; スパイラルスリット; 溶接残留応力; PILATUS

A diffraction spot trace method (DSTM) was proposed. The DSTM is a new technique to measure internal stresses, which combined a special rotating slit system and an area de-tector (PILATUS). The enough collimation of the special rotating slit system was examined from measuring the bending stress in a specimen of S45C. The bending stresses in the specimens of aluminum and magnesium alloys were measured using the DSTM. The ob-tained stress distributions corresponded with the applied stresses. The DSTM was applied to the measurement of the welding residual stresses. The residual stress map by the DSTM corresponded with the simulated results by a finite element method.

提出了一种衍射斑跟踪方法(DSTM)。DSTM是一种新型的内应力测量技术，它结合了特殊的旋转狭缝系统和面积衰减器(Pilatus)。通过对S45C试件弯曲应力的测量，验证了特殊旋转缝隙系统的准直性。利用差示扫描量热仪(DSTM)测量了铝合金和镁合金试件的弯曲应力。得到的应力分布与所施加的应力相对应。将数字扫描隧道显微镜应用于焊接残余应力的测量。DSTM得到的残余应力图与有限元模拟结果吻合较好。

项目成果

放射光による溶接材の内部残留応力評価

使用同步辐射评估焊接材料的内部残余应力

• 发表时间: 2013
• 作者: 鈴木賢治;菖蒲敬久;城鮎美;張朔源
• 通讯作者: 張朔源

ウォータジェットピーニングを受けたオーステナイト系ステンレス鋼の残留応力

奥氏体不锈钢经水喷射喷丸后的残余应力

• 发表时间: 2013
• 期刊: 材料
• 作者: 鈴木賢治;菖蒲敬久;城鮎美
• 通讯作者: 城鮎美

2次元検出器を利用した粗大粒の内部応力評価

使用二维检测器评估粗晶粒的内应力

• 发表时间: 2013
• 作者: 鈴木賢治;菖蒲敬久;城鮎美;張朔源
• 通讯作者: 張朔源

Internal stress measurement of weld part using diffraction spot trace method

衍射点迹法测量焊缝内应力

• 发表时间: 2014
• 期刊: Materials Science Forum
• 作者: K. Suzuki;T. Shobu;A. Shiro and S. Zhang
• 通讯作者: A. Shiro and S. Zhang

回折斑点追跡法による粗大粒の内部応力評価

利用衍射点跟踪法评价粗晶粒的内应力

• 发表时间: 2013
• 作者: 鈴木賢治;菖蒲敬久;城鮎美;張朔源
• 通讯作者: 張朔源