Developments of CFRP structures with electricity storagepotential

具有储电潜力的CFRP结构的发展

• 批准号: 22560683
• 负责人: FUKUDA Hiroshi
• 金额: $ 2.83万
• 依托单位: Tokyo University of Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560683/
• 关键词: 構造・機能材料; 複合効果; 複合材料・物性

Throughout the present research for developing CFRP structures with electricity storage potential, the following results have been obtained:1) Thin Li-ion secondary battery could be stably fabricated;2) Mechanism of interlaminar fracture causedby embedding thin films in CFRP laminates could be made clear at some amount;3) Charge/discharge properties of the secondary battery under high-to-low temperature region were examined, showing the possibility and subjects of the battery for aerospace use;4) Possibility and limit of usage under mechanical strain of secondary battery-embedded CFRPs were demonstrated.

通过目前开发具有储电潜力的CFRP结构的研究，已经获得以下结果：1）可以稳定地制造薄型锂离子二次电池；2）在CFRP层压板中嵌入薄膜引起层间断裂的机制可以在一定程度上得到阐明；3）研究了二次电池在高低温区域下的充放电性能，展示了该电池用于航空航天的可能性和主题；4） 论证了二次电池嵌入式 CFRP 在机械应变下使用的可能性和限制。

项目成果

蓄電機能を有するCFRPの成形法の検討

具有蓄电功能的CFRP成型方法研究

• 发表时间: 2011
• 作者: 齊藤和也;E.関谷;見波大輝;成田駿介
• 通讯作者: 成田駿介

All Solid Thin-Filmed Li-Ion Rechargeable Battery with Aligned Carbon Nanotube Anode

定向碳纳米管阳极全固态薄膜锂离子充电电池

• 发表时间: 2012
• 作者: M. Baba(馬場守); F. Izumida; R. Ye(叶榮彬); J. Yoshida; T. Ushirokawa; K. Ohta and M. Kusunoki
• 通讯作者: K. Ohta and M. Kusunoki

蓄電機能を有する CFRP の開発

具有蓄电功能的CFRP的开发

• 发表时间: 2012
• 作者: 小山昌志;成田駿介; 福田博; 八田博志;肖毅; 叶榮彬
• 通讯作者: 叶榮彬

Numerical analysis of delamination in composite laminates with embedding devices

使用嵌入装置对复合材料层压板分层进行数值分析

• 发表时间: 2012

蓄電機能を有する CFRP の成形法の検討

具有蓄电功能的CFRP成形方法研究

• 发表时间: 2011
• 作者: 小山昌志;成田駿介; 福田博; 八田博志;肖毅;叶榮彬;馬場守
• 通讯作者: 馬場守