Gas Recycling Process of Magnesium Alloy Scrap

镁合金废料气体回收工艺

• 批准号: 22560743
• 负责人: INOUE Makoto
• 金额: $ 3.08万
• 依托单位: National Institute of Technology, Toyama College
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560743/
• 关键词: リサイクル; マグネシウム; 真空蒸留法; 押出加工; マグネシウム合金; 押出加工法; 機械的特性; 耐食性

Gas recycling of the magnesium alloy by the vacuum distillation examined in distillation time 2-5h for raw materials temperature 600℃, condense temperature310-350℃, and there was not the clear difference in this condense temperature range. The extrusion load grew big so that I examined the production condition of extrusion temperature 350-400 ℃ of the extrusion, extrusion ratio R8-16 as gas recycling materials provided in vacuum distillation, and extrusion temperature was low or so that the extrusion ratio was big. Raw materials Mg-Al-Zn alloy was harder than raw materials Mg-Al-Mn alloy, and the hardness of magnesium gas recycling extrusions, the strength came to have a big strength. The corrosion resistance was good, and the influence of the extrusion temperature did not have the clear difference.

对镁合金真空蒸馏回收气体进行了研究，在原料温度600℃，冷凝温度310 -350℃，蒸馏时间2- 5 h，在此冷凝温度范围内无明显差异。由于挤压负荷变大，因此我考察了挤压温度为350-400 ℃，挤压比为R8-16的生产条件，作为真空蒸馏中提供的气体回收材料，挤压温度低或挤压比大。原材料Mg-Al-Zn合金比原材料Mg-Al-Mn合金硬度高，且镁合金气回收挤压件的硬度、强度都有较大的提高。耐腐蚀性能良好，挤压温度对合金的影响无明显差异。

项目成果

High-Purity Gas Recycling of Mg-Al-Mn Alloy

镁铝锰合金高纯气体回收

• 发表时间: 2012
• 作者: 片野有規;滝山博志;井上誠;井上 誠;井上誠
• 通讯作者: 井上誠

マグネシウム合金のリサイクル

镁合金回收

• 发表时间: 2010
• 作者: 井上誠;島政司;松澤和夫;会田哲夫;古井政明;井上誠
• 通讯作者: 井上誠

Mg-Al-Zn 合金の気相リサイク ル

Mg-Al-Zn合金的气相回收

• 发表时间: 2011
• 作者: 片野有規;滝山博志;井上誠;井上 誠;井上誠;井上誠;井上誠
• 通讯作者: 井上誠

Mg-Al-Zn合金の気相リサイクル

Mg-Al-Zn合金的气相回收

• 发表时间: 2011
• 作者: 井上誠;島政司;松澤和夫;会田哲夫;古井政明
• 通讯作者: 古井政明

マグネシウム合金の気相リサイクル

镁合金的气相回收

• 发表时间: 2010
• 作者: 井上誠;島政司;松澤和夫;会田哲夫;古井政明
• 通讯作者: 古井政明